Super Duplex 2507 · ISO 16143-1
Super Duplex 2507 is presented here as X2CrNiMoN25-7-4 (4410-327-50-E) under ISO 16143-1. Technical delivery requirements for corrosion-resistant stainless steel flat products for general purposes.
X2CrNiMoN25-7-4
Designation: 4410-327-50-E
Data edition: ISO 16143-1:2014
Super Duplex 2507 4410-327-50-E
Super Duplex 2507 is presented here as X2CrNiMoN25-7-4 (4410-327-50-E) under ISO 16143-1. Technical delivery requirements for corrosion-resistant stainless steel flat products for general purposes.
Table 1 chemistry from ISO 16143-1:2014. Room-temperature Tables 4 and 5 are cross-checked using the PSQCA adoption PS-ISO 16143-1:2015. Duplex 2205 and S31803 use the same ISO designation here; this is not a claim of UNS S32205 equivalence.
Related grades
12 material references with ISO 16143-1 data.
Super Duplex 2507 properties
Select a table to compare requirements.
| Element | Mass % |
|---|---|
| C | ≤0.030 |
| Si | ≤1.00 |
| Mn | ≤2.00 |
| P | ≤0.035 |
| S | ≤0.015 |
| Cr | 24.0–26.0 |
| Ni | 6.0–8.0 |
| Mo | 3.0–4.5 |
| N | 0.24–0.35 |
| Other elements | — |
Composition in mass %. ≤ denotes a maximum; ≥ denotes a minimum; paired values are ranges. — means no numerical limit is provided in the cited data, not zero.
| Form | Thickness (mm) | Condition | Test direction | Rp0.2 (MPa) | Rp1.0 min (MPa) | Rm (MPa) | A80 min (%) | A min (%) | Other requirements |
|---|---|---|---|---|---|---|---|---|---|
| Cold-rolled strip | ≤6 | +AT | Transverse | 550 | — | ≥750 | 15 | 15 | — |
| Hot-rolled strip | ≤12 | +AT | Transverse | 530 | — | ≥750 | 15 | 15 | — |
| Hot-rolled plate | ≤75 | +AT | Transverse | 530 | — | ≥730 | 20 | 20 | — |
Room-temperature properties for the stated product form and condition. Proof strengths and elongation are minima unless a range is shown. A80 uses an 80 mm gauge length below 3 mm thickness; A uses 5.65√S₀ from 3 mm thickness. +AT means solution annealed. For strip below 300 mm width tested longitudinally, proof stress is reduced by 15 MPa; austenitic A80 is reduced by 5 percentage points and A by 2 points. Stretcher-levelled SS304 elongation is 5 points lower. +AT2 is an alternative supplied only by agreement.